| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 0.04 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.39-1.43 | ||
| 玻璃纖維含量 | Ash | 15 | % | ||
| 成型收縮率 | ASTM D-955 | 0.2-1.4 | % | ||
| 機(jī)械性能 | IZOD沖擊強(qiáng)度 | ASTM D-256 | 5-7 | Kg.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 93 | M-Scale | ||
| 引張伸長(zhǎng)率 | ASTM D-638 | 4-5 | % | ||
| 撓曲強(qiáng)度 | ASTM D-790 | 1300-1500 | Kg/cm2 | ||
| 撓曲彈性率 | ASTM D-790 | 40000-50000 | Kg/cm2 | ||
| 引張強(qiáng)度 | ASTM D-638 | 800-1000 | Kg/cm2 | ||
| 電氣性能 | 表面電阻率 | ASTM D-257 | >1014 | Ω | |
| 誘電正接 | 60Hz | ASTM D-150 | 0.001 | ||
| 絕緣破壞強(qiáng)度 | ASTM D-149 | 20 | KV/mm | ||
| 體積電阻率 | ASTM D-257 | >1016 | Ω.cm | ||
| 誘電率 | 60Hz | ASTM D-150 | 3.3 | ||
| 耐電弧性 | ASTM D-495 | 129 | sec | ||
| 熱性能 | 熱變形溫度 | 4.6Kg/cm2 | ASTM D-648 | 220 | ℃ |
| 線膨脹系數(shù) | ASTM D-696 | 5 | 10-5cm/cm℃ | ||
| 熔點(diǎn) | DSC | 225 | ℃ | ||
| 熱變形溫度 | 18.6Kg/cm2 | ASTM D-648 | 206 | ℃ | |
| 耐燃性 | 0.83mm | UL 94 | HB | ||
PBT性質(zhì)：為高結(jié)晶性熱可塑性塑料，熔點(diǎn)220~230℃，結(jié)晶速率比PET快。
PBT優(yōu)點(diǎn)：機(jī)械性質(zhì)安定抗張強(qiáng)度與抗張模數(shù)和尼龍相似、摩擦系數(shù)小有自潤(rùn)性、吸水率低、電氣性質(zhì)優(yōu)良、尺寸安定性良好、耐藥品性、耐油性極佳。缺 點(diǎn)：Tg(30℃)低，在荷重下H.D.T.為60℃、抗沖擊強(qiáng)度不良，一般以玻纖補(bǔ)強(qiáng)為FR-PBT來(lái)使用.
PBT用 途：1)、電子電器：無(wú)熔線斷電器、電磁開(kāi)關(guān)、馳返變壓器、家電把手、連接器、外殼. 2)、汽車： 車門把手、保險(xiǎn)桿、分電盤蓋、擋泥板、導(dǎo)線護(hù)殼、輪圈蓋工業(yè)零件：OA風(fēng)扇、鍵盤、釣具卷線器、零件、燈罩.
PBT 基礎(chǔ)創(chuàng)新塑料(美國(guó)) SABIC Valox PBT(聚對(duì)苯二甲酸丁二醇脂)：
Valox DR51M特性：15％玻璃纖維增強(qiáng)型PBT.機(jī)械/熱/電氣性能強(qiáng); 阻燃.用于聚光燈,家電外殼和處理.易流動(dòng),易脫模.
PBT理化特性 : PBT為乳白色半透明到不透明、結(jié)晶型熱塑性聚酯。具有高耐熱性、韌性、耐疲勞性，自潤(rùn)滑、低摩擦系數(shù)，耐候性、吸水率低，僅為0.1%，在潮濕環(huán)境中仍保持各種物性（包括電性能），電絕緣性，但體積電阻、介電損耗大。耐熱水、堿類、酸類、油類、但易受鹵化烴侵蝕，耐水解性差，低溫下可迅速結(jié)晶，成型性良好。缺點(diǎn)是缺口沖擊強(qiáng)度低 ，成型收縮率大 。故大部分采用玻璃纖維增強(qiáng)或無(wú)機(jī)填充改性，其拉伸強(qiáng)度、彎曲強(qiáng)度可提高一倍以上，熱變形溫度也大幅提高。可以在140℃下長(zhǎng)期工作，玻纖增強(qiáng)后制品縱、橫向收縮率不一致，易使制品發(fā)生翹曲。